| Testing |
屬性名稱 |
測試方法 |
測試條件 |
Unit |
代表值 |
|
| 機械特性 |
Izod 沖擊強度(Notched) |
ASTM D256 |
1/8″,23℃ |
kg·cm/cm
|
35
|
| Izod 沖擊強度(Notched) |
ASTM D256 |
1/8″,-30℃ |
kg·cm/cm
|
19
|
| Izod 沖擊強度 |
ASTM D256 |
1/4″,23℃ |
kg·cm/cm
|
30
|
| 拉伸模量 |
ASTM D638 |
50mm/min |
kg/?
|
21800
|
| Izod 沖擊強度(Notched) |
ASTM D256 |
1/4″,-30℃ |
kg·cm/cm
|
19
|
| 斷裂點拉伸率 |
ASTM D638 |
50mm/min |
%
|
30
|
| 屈服點的伸長率 |
ASTM D638 |
50mm/min |
%
|
>6
|
| 彎曲強度 |
ASTM D790 |
15mm/min |
kg/?
|
780
|
| 拉伸強度 |
ASTM D638 |
50mm/min |
kg/?
|
490
|
| 彎曲模量 |
ASTM D790 |
15 mm/min |
kg/?
|
24000
|
| 熱力特性 |
熱變形溫度 |
ASTM D648 |
1/4″,18.5kg/?(unannealed) |
?C
|
88
|
| 熱變形溫度 |
ASTM D648 |
1/4″,4.6kg/?(annealed) |
?C
|
96
|
| 熱變形溫度 |
ASTM D648 |
1/4″,4.6kg/?(unannealed) |
?C
|
94
|
| 維卡軟化點 |
ASTM D1525 |
1kg |
?C
|
103
|
| 熱變形溫度 |
ASTM D648 |
1/4″,18.5kg/?(annealed) |
?C
|
90
|
| 維卡軟化點 |
ASTM D1525 |
5kg, 50℃/hr |
?C
|
99
|
| 物理特性 |
比重 |
ASTM D792 |
23℃ |
|
1.05
|
| 成型收縮率 |
ASTM D955 |
- |
%
|
0.4~0.7
|
| 流動系數 |
ASTM D1238 |
220℃/10kg |
g/10min
|
19.5
|
| 流動系數 |
ASTM D1238 |
230℃/3.8kg |
g/10min
|
6.8
|
| 熔融指數 |
ASTM D1238 |
200℃/5kg |
g/10min
|
1.9
|
| 電學特性 |
HVTR |
UL746A |
PCL Code |
|
2
|
| HAI |
UL 746A |
PCL Code |
|
0
|
| CTI |
UL746A |
PCL Code |
|
0
|
| Arc Resistance |
ASTM D495 |
PCL Code |
|
5
|
| HWI |
UL 746A |
PCL Code |
|
3
|
| 阻燃特性 |
阻燃性 |
UL94 |
1/8" |
class
|
HB
|
| 阻燃性 |
IEC707 |
1/8" |
㎜/min
|
FH3-33
|
| 阻燃性 |
UL94 |
1/16" |
Class
|
HB
|
|
|